Poly(glycolic acid)/poly(alkylene glycol) block copolymers and method of manufacturing the same
Surgical materials and devices
Filament material polylactide mixtures
Resorbable implantable device for the reconstruction of the orbit of the human skull
Resorbable tendon and bone augmentation device
Oriented polyglycolic acid film and production process thereof
Biodegradable implant material comprising bioactive ceramic
Device for incorporation and release of biologically active agents
Method for the production of polyglycolic acid
Process for forming bioabsorbable implants Patent #: 6719935
ApplicationNo. 10472908 filed on 01/31/2003
US Classes:606/76, Specialized coating or material264/177.17, Processing or treatment after extrusion (e.g., support, guide, etc.)264/177.19, Temperature specified (other than ambient)264/178F, Filaments264/210.5, With temperature gradient across cross-section of workplace or heat treatment after all shaping264/210.7, Plural stretching steps or stages264/210.8, Of filament264/211.12, Processing or treatment after extrusion525/450, Solid polymer derived from hydroxy-containing carboxylic acid or derivative reactant528/361, From ether, metal alcoholate, or alcohol group-containing carboxylic acid; or from a derivative of a carboxylic acid which derivative contains an ether, metal alcoholate, or alcohol group528/502B, Stretching to alter polymer properties by elongation528/502R, Physical treatment528/86, FROM PHENOL, PHENOL ETHER, OR INORGANIC PHENOLATE606/77, Absorbable524/108, Two or more chalcogen atoms in the same hetero ring623/17.18, Facial bone606/232, Suture retaining means (e.g., buttons)523/113, Composition suitable for use as tissue or body member replacement, restorative, or implant427/2.27, Inorganic oxygen-containing compound containing layer formed (e.g., hydroxyapatite, ceramic, glass)528/354, From compound having -C-C(=O)-O-C- group as part of a heterocyclic ring, e.g., lactone, etc.264/40.7Controlling rate of movement of molding material or its support in a continuous process
ExaminersPrimary: Feely, Michael J
Attorney, Agent or Firm
International ClassesA61F 2/00
The present invention relates to polymer compositions andartefacts made therefrom. In particular the present invention relates to polymers having high mechanical strength and their use for the manufacture of load bearing medical devices suitable for implantation within the body. More particularly theinvention relates to bioresorbable poly-glycolic acid-containing polymers and to implantable medical devices made therefrom.
Polymer compositions comprising poly-glycolic acid (PGA) have an established use for medical implants. It has also been proposed that certain mechanical properties may be improved by extruding PGA melts or by drawing PGA in a plastic state. Isotropic PGA has a tensile strength of between 50 to 100 MPa and a tensile modulus of between 2 and 4 GPa. A commercial product (SR-PGA) comprising PGA fibres in a PGA matrix has a flex strength and modulus of 200-250 MPa and 12-15 GPa, respectively. It is also reported in the literature that melt spun PGAs have tensile strength of about 750 MPa and a modulus of from 15 to 20 GPa. In U.S. Pat. No. 4,968,317 an example of a drawn PGA is stated to have a tensile strength of about 600 MPa.
Although PGAs having improved strength characteristics are known,. none of the known materials have the mechanical properties approaching those of the metals conventionally used for load bearing implantable medical devices. A commercial alloyused for orthopaedic implant devices, known as Ti-6-4, comprises titanium with 6% aluminium and 4% vanadium and has a tensile strength in the range of 800 to 1000 MPa and a modulus in the order of 1000 Pa.
One possible reason that PGA cannot currently be processed to achieve the desired strength of metals is that when PGA is processed by common methods to produce orientated fibres (e.g. stretching the material at a constant rate in a heated chamberor tank) additional crystallisation of the polymer occurs during the process. The crystals in the polymer act such that they prevent further orientation of the polymer. This crystallisation of the polymer limits the mechanical properties that can beachieved by drawing PGA to around 800 MPa, as described in the prior art.
We have found that polymer compositions comprising PGA may be processed such that the resultant composition has significantly greater strength, typically of the order of greater than 1200 MPa with a commensurate increase in modulus, typically inexcess of 22 GPa.
In accordance with the present invention there is provided a polymer composition comprising poly-glycolic acid or a functional derivative thereof having a tensile strength of at least 1200 MPa.
The polymer composition gains this level of tensile strength by means of a novel processing method that results in an orientated structure, for example an orientated fibre.
The present invention further provides an artefact comprising a polymer composition including poly-glycolic acid or a functional derivative thereof having a tensile strength of at least 1200 MPa.
The polymer composition may be comprised entirely of PGA or a derivative thereof, or may comprise a PGA-containing blend with other polymers. Preferably the polymer composition is entirely PGA.
Similarly, artefacts formed from the polymer compositions of the invention may consist wholly of the polymer compositions of the invention or may be composites consisting only partially of the polymer compositions of the invention.
Aptly the artefact contains 10 to 80% by volume of the polymer compositions of the invention, suitably the artefact contains up to 60% by volume of the polymer compositions of the invention, preferably the artefact contains at least 40% by volumeof the polymer compositions of the invention and typically the artefact contains approximately 50% by volume of the polymer compositions of the invention.
BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS
FIG. 1 depicts an embodiment wherein the fibre is locally heated.
FIG. 2 depicts an embodiment wherein the fibre is drawn by a weight.
FIG. 3 shows strength and modulus values in relation to zone temperature.
FIG. 4 shows a two-part mould for a fixation plate.
FIG. 5 shows a two-part mould for a RCI screw.
DETAILED DESCRIPTION OF THE INVENTION
We have found that in order to achieve the high strength exhibited by the compositions of the invention it is necessary that the PGA be rendered into an amorphous state and then immediately drawing to form a highly orientated structure.
This can be achieved by first processing isotropic PGA granules, which are commercially available, to form fibres or filaments, thereafter passing the fibres into a quenching bath to form an amorphous structure. Polymer compositions of thepresent invention may then be produced by drawing the quenched, amorphous PGA. Preferably this is a drawing process which minimises the time polymer is exposed to elevated temperatures, thus minimising the time for the polymer to crystallise.
In accordance with another aspect of the invention there is provided a process for the manufacture of poly-glycolic acid-based polymer compositions comprising increasing polymer chain orientation of a substantially amorphous polymer by drawing atlocalized points within the mass.
Suitably this comprises the steps of forming poly-glycolic acid or a functional derivative thereof into fibres, for example by melt extrusion or solution spinning; quenching the fibres then subjecting the quenched fibres to a tension underconditions whereby a defined region of the tensioned fibres is drawn.
Aptly fibres of amorphous PGA-containing polymers may be prepared by solution spinning or melt extruding the polymer through a die; the filament is then rapidly chilled to produce a substantially amorphous material. Typical chilling methodsinclude blowing a cold gas onto the filament as it is produced or by passing the filament through a bath of a suitable cold liquid, e.g. water, silicone oil.
A suitable drawing method is zone heating. In this process a localised heater is moved along a length of fibre which is held under constant tension. This process is used in the zonedrawing process as described by Fakirov in Oriented PolymerMaterials, S Fakirov, published by Huthig & Wepf Verlag, Huthig GmbH. In order to carry out this zone heating fibre can be passed through a brass cylinder. A small part of the cylinder inner wall is closer to the fibre, this small region locally heatsthe fibre, compared to the rest of the brass cylinder, localising the drawing of the fibre to this location, see FIG. 1. A band heater can be placed around the brass cylinder to allow it to be heated above room temperature. This heated brass cylindercan then be attached to the moving cross-head of a tensile testing machine and the fibre to be drawn suspended from a beam attached to the top of the testing machine. To draw the fibre a weight can be attached to the lower end of the fibre, the brasscylinder heated to the desired temperature and the cross-head moved to the lower end of the fibre, see FIG. 2. The polymer draws where the fibre is closest to the brass cylinder, as the cross-head is moved up the length of the fibre, then a length ofthe fibre can be drawn.
Suitably the fibre can be held taut using a small stress, which is typically below the yield point of the material at ambient temperatures. The fibre can then be heated locally to a temperature which is above the softening point (Tg) butbelow the melting point such that localised drawing of the polymer occurs, the whole fibre can be treated by movement of either or both the fibre and heated zone such that the full length of the fibre is drawn. This first drawing of the polymer mayproduce a polymer with improved molecular alignment and therefore strength and modulus. In this first step the conditions are selected such that the material does not substantially crystallise during the process, this requires that either thetemperature of the polymer is below the temperature at which crystallisation occurs, Tc, or if the polymer is above Tc the speed at which the heated zone moves along the fibres is fast enough such that the polymer cools below Tc before ithas time to crystallise. Further improvements can be made by subsequent treatments, where the stress applied to the fibre or the zone temperature is increased or both. Both the strength of the fibre and the softening point increase as the degree ofmolecular alignment improves. The process can be repeated many times, until the desired properties are reached. A final annealing step can be carried out in which the material crystallises under tension in the process; this can further improve themechanical properties and improve the thermal stability of the final fibre.
In an embodiment of this aspect of the invention there is provided an artefact comprising a poly-glycolic acid in accordance with the invention. For example, the poly-glycolic acid fibres can be mixed with other components to form the artefacts. These other components may be polymers, co-polymers, bioresorbable polymers, non-polymeric materials or combinations thereof.
Aptly the bioresorbable polymer comprises a poly-hydroxy acid, a poly-lactic acid, a poly-caprolactone, a polyacetal, a poly-anhydride or mixture thereof; the polymer comprises poly-propylene, poly-ethylene, poly-methyl methacrylate, epoxy resinor mixtures thereof whilst the non-polymeric component comprises a ceramic, hydroxyapatite, tricalcium phosphate, a bioactive factor or combinations thereof.
Suitably the bioactive factor comprises a natural or engineered protein, a ribonucleic acid, a deoxyribonucleic acid, a growth factor, a cytokine, an angiogenic factor or an antibody.
Artefacts according to the present invention can aptly be manufactured by placing appropriate lengths of strengthened PGA fibre into moulds, adding the other components then compression moulding. Alternatively, the strengthened fibres can bepre-mixed with the other components then compression moulded.
In an alternative processing method, artefacts according to the present invention can be manufactured by forming a polymeric component in the presence of the strengthened fibres by in situ curing of monomers or other precursors for said polymericcomponent.
Preferably the monomers used in this process do not liberate any by-products on polymerisation as these can compromise the properties of the artefact.
Aptly at least one of the monomers used in said in situ curing process is a ring-opening monomer that opens to form a poly-hydroxy acid. Typically at least one monomer is a lactide, a glycolide, a caprolactone, a carbonate or a mixture thereof.
The polymer compositions of the invention are useful for the production of medical devices, particularly implantable devices where it is desirable or necessary that the implant is resorbed by the body. Thus, artefacts in accordance with thepresent invention include sutures; tissue-engineering scaffolds or scaffolds for implantation; orthopaedic implants; reinforcing agents for long fibre composites used in resorbable load bearing orthopaedic implants; complex shaped devices, for exampleformed by injection moulding or extruding composites formed by mixing short lengths of chopped fibres with poly-lactic acid; or bone fixation devices, for example formed from relatively large diameter rods (e.g., greater than 1 mm) of the compositions ofthe invention.
The invention will now be illustrated by the following examples.
Isotropic PGA was extruded into a water bath to produce a translucent fibre of approx 0.5 mm diameter. This fibre was then suspended vertically and a weight of 200 g was applied. A heated cylinder of brass with a hole of approx 15 mm apart froma small section with a 2 mm diameter hole, through which the PGA fibre passes, was heated to a temperatures between 70° C. and 100° C. and moved along the fibre at a speed of 300 mm/min. The fibres were still translucent after thisprocess, with the exception of the fibre processed with the bass cylinder set to a temperature of 100° C. which was opaque. The resultant fibres were tested by mounting them at 22° C. in a Zwick tensile testing machine, such that thelength of fibre between the grips was 40 mm. The sample was then pulled at a rate of 10 mm/min. The resultant load extension curve was recorded and the maximum load recorded was used to calculate the maximum strength of the fibre and the initial slopewas used to calculate the modulus of the sample. The results are shown in FIG. 3.
Isotropic PGA was extruded into a water bath to produce a translucent fibre of approx 0.5 mm diameter. This fibre was then suspended vertically and a weight of 200 g was applied. A heated cylinder of brass with a hole of approx 15 mm apart froma small section with a 2 mm diameter hole, through which the PGA fibre passes, was heated to a temperature of 90° C. and moved along the fibre at a speed of 500 mm/min. The resultant fibre was still translucent after this process. The fibreproduced was tested, as described below, and found to have a strength of 1780 MPa and a modulus of 26.7 GPa.
PGA fibre was produced as in example 2, and then the drawn PGA fibre was re-drawn using a temperature of 90° C. and a speed of 500 mm/min for the zone, with a weight of 500 g applied to the fibre. The fibre produced was opaque indicatingthat crystallization of the polymer had occurred in this process step. When tested the fibres were found to have a strength of 2400 MPa and a modulus of 40.8 GPa.
A block of PTFE was machined to form a two-part mould for a fixation plate, see FIG. 4. A reaction mixture was prepared by weighing 100 g of DL-Lactide into a glass vial in a dry nitrogen atmosphere and sealed with a septum. 10 μl of asolution of SnCl2.2H2O (1.00 g) in Di(ethylene glycol) (2.91 g) were then injected into the monomer vial using a 25 μl syringe. The vial was then heated in an oven at 150° C., once the monomer had completely melted; the vial was shaken to mixthe contents. Braided fibres of drawn PGA, as made in Example 2, were first packed into the mould cavity (corresponding to 45% of the mould volume) and then the mould was placed in an oven at 150° C. Once the mould at reached temperature, themolten reaction mixture and mould were placed in a dry nitrogen atmosphere and the reaction mixture poured into the mould before either had cooled sufficiently for the monomer to crystallise. The filled mould was sealed then returned to the 150° C. oven, vented by piercing the cap with a syringe needle. To remove air bubbles from the fibre in the mould, the hot mould was transferred to a vacuum oven at 150° C. A vacuum of 1 mbar was applied, the oven was then re-pressurised with drynitrogen; this was repeated once. The mould was then removed from the oven and the syringe needle vent removed. The mould was then placed in a conventional oven at 150° C. for 6 days to cure the polymer.
After curing the mould was removed from the oven and allowed to cool to room temperature. The mould was then separated and the device removed from the mould. The DL-lactide had polymerized to form a translucent solid phase around the fibres.
Using the same mould as for example 4 a fixation plate was made using L-lactide as the monomer precursor for the matrix. The catalyst, initiator and curing conditions were identical to those used in example 4. When the plate was removed fromthe mould it could be seen that the L-lactide had polymerized to form an opaque solid around the fibres.
A block of PTFE was machined to form a two-part mould for a RCI screw, see FIG. 5. The catalyst, initiator and curing conditions used were identical to example 4 but the material used to form the matrix was a mixture of DL-lactide and glycolidein the ratio 85:15. Short fibres of drawn PGA (approx 2 mm long), as made in example 2, were packed into the mould (corresponding to 30% of the mould volume). Once curing was complete the mould was left to cool and the device removed. The monomers hadcured to form a solid translucent phase around the fibres.
* * * * *
Field of SearchBy calendering
Shaping by extrusion
Processing or treatment after extrusion (e.g., support, guide, etc.)
Temperature specified (other than ambient)
With reinforcement filler, or additive
With temperature gradient across cross-section of workplace or heat treatment after all shaping
Plural stretching steps or stages
Processing or treatment after extrusion
Screw extruder or screw feeder device
Solid polymer derived from hydroxy-containing carboxylic acid or derivative reactant
From ether, metal alcoholate, or alcohol group-containing carboxylic acid; or from a derivative of a carboxylic acid which derivative contains an ether, metal alcoholate, or alcohol group
Stretching to alter polymer properties by elongation
Specialized coating or material