| Number | Title | Issue Date |
| 7665678 | Method for producing fine denitrided metal particles using grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 02/23/2010 |
| 7578457 | Method for producing fine dehydrided metal particles using grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 08/25/2009 |
| 7416141 | Method for producing diamond particles using grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 08/26/2008 |
| 7329303 | Methods for producing titanium metal using grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 02/12/2008 |
| 7267292 | Method for producing fine alumina particles using multi-carbide grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 09/11/2007 |
| 7213776 | Method of making particles of an intermetallic compound Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 05/08/2007 |
| 7140567 | Multi-carbide material manufacture and use as grinding media Grinding media, including shaped media such as spheres or rods ranging in size from about 0.5 micron to 100 mm in diameter, are formed from a multi-carbide material consisting essentially of two or more carbide-forming elements and carbon, with or without carbide-fo... | 11/28/2006 |